Understanding metal dissolution from solar photovoltaics in MSW leachate under standard waste characterization conditions for informing end-of-life photovoltaic waste management

The upcoming end-of-life solar photovoltaics (PV) waste stream is a huge concern before solid waste professionals due to presence of hazardous metals like lead or cadmium. The objective of present study was to understand the metal dissolution from PVs under four standard waste characterization regulatory tests of U.S., Germany, and Japan and their representativeness with actual landfill leachate. Modules were exposed to real municipal solid waste (MSW) landfill leachate for extended extraction duration, agitation and diluted leachate to investigate the effect of various parameters on metal dissolution. The results indicated that extractions using landfill leachates resulted in lower metal release than standard methods. The leached metal concentrations were found to be within the threshold limits except for cadmium, copper, lead and selenium, with maximum lead release from amorphous-PV of 8.68 mg/L and 6.91 mg/L with respect to TCLP and WET tests, respectively. Arsenic showed negligible release with maximum concentration of 0.046 mg/L from copper indium gallium de-selenide(CIGS) PV. Regardless of small size (1–2 cm pieces) and agitation, Germany and Japan's standard tests resulted in minimal release except of copper from copper indium gallium de-selenide PV. Leaching without agitation, showed negligible release from all photovoltaics whereas when agitation is applied to diluted leachate, significant release was observed with aluminum and copper leached up to 145.32 mg/L (multi-crystalline silicon) and 139.01 mg/L (amorphous-PV), respectively. CIGS was found to be most hazardous with a Metal Hazard Score (calculated on the basis of magnitude of leached metals with respect to their threshold limit and subsequent health effects) of 23.19, when exposed to standard tests. For all scenarios, increased metal release was observed with decrease in sample size and increase in leachate dilution and thus, leaching in highly acidic conditions are by no means representative for modules dumping in realistic conditions.