Tribocorrosion of stainless steel sliding against graphite in FLiNaK molten salt

Xin He; Chanaka Kumara; Dino Sulejmanovic; James R. Keiser; Nidia Gallego; Jun Qu

doi:10.1016/j.wear.2023.204706

Tribocorrosion of stainless steel sliding against graphite in FLiNaK molten salt

Xin He, Chanaka Kumara, Dino Sulejmanovic, James R. Keiser, Nidia Gallego, Jun Qu

Research output: Contribution to journal › Article › peer-review

4 Scopus citations

Abstract

The molten salt reactor (MSR) concept recently gained renewed interest in developing Generation IV nuclear reactors. One MSR design uses fluoride molten salts to cool tri-structural isotropic particle fuel encapsulated by a carbon matrix into spherical pebbles, which would inevitably contact the reactor's stainless steel container wall during salt circulation. Characterizing this interaction is crucial for reactor safety. Here we report the tribocorrosion behavior of graphite sliding against Type 316H stainless steel lubricated by a FLiNaK (LiF:NaF:KF; 46.5:11.5:42 mol %) molten salt in an argon environment. Accelerated wear loss was observed at a higher temperature because of a lower molten salt viscosity and a higher corrosion rate. The graphite had a more rapid material loss at a higher sliding speed than stainless steel because of its higher vulnerability to vibration-induced microfracture. The salt-starved condition caused more material loss than either the no-salt or the salt-flooded condition because neither a graphite transfer film nor stable boundary lubrication could be established at salt starvation. An interesting dual-layer surface film was discovered on the stainless steel worn surface: a chromium-rich top film and a nickel-accumulated but chromium-depleted interlayer. The film composition and structure provide fundamental insights to the mechanochemical interactions between stainless steel and graphite in a molten salt environment.

Original language	English
Article number	204706
Journal	Wear
Volume	522
DOIs	https://doi.org/10.1016/j.wear.2023.204706
State	Published - Jun 1 2023

Funding

Authors thank G. Meric from Kairos Power for providing graphite pebbles and discussing testing conditions, K. Cooley from ORNL for help on test setup, D. Loposser and D. Wilson from ORNL for electronic repair of the tribometer, and B. Qu from Oak Ridge High School for programming an app for removing the noise signal from the acquired frictional data. Research sponsored by the US Department of Energy, Office of Nuclear Energy, Advanced Reactor Technology Program. This manuscript has been authored by UT-Battelle, LLC, under contract DE-AC05-00OR22725 with the US Department of Energy (DOE). The US government retains and the publisher, by accepting the article for publication, acknowledges that the US government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish or reproduce the published form of this manuscript, or allow others to do so, for US government purposes. DOE will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan (http://energy.gov/downloads/doe-public-access-plan). Authors thank G. Meric from Kairos Power for providing graphite pebbles and discussing testing conditions, K. Cooley from ORNL for help on test setup, D. Loposser and D. Wilson from ORNL for electronic repair of the tribometer, and B. Qu from Oak Ridge High School for programming an app for removing the noise signal from the acquired frictional data. Research sponsored by the US Department of Energy, Office of Nuclear Energy , Advanced Reactor Technology Program. This manuscript has been authored by UT-Battelle, LLC, under contract DE-AC05-00OR22725 with the US Department of Energy (DOE) . The US government retains and the publisher, by accepting the article for publication, acknowledges that the US government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish or reproduce the published form of this manuscript, or allow others to do so, for US government purposes. DOE will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan ( http://energy.gov/downloads/doe-public-access-plan ). This manuscript has been authored by UT-Battelle, LLC, under contract DE-AC05-00OR22725 with the US Department of Energy (DOE). The US government retains and the publisher, by accepting the article for publication, acknowledges that the US government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish or reproduce the published form of this manuscript, or allow others to do so, for US government purposes. DOE will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan ( http://energy.gov/downloads/doe-public-access-plan ).

Keywords

Graphite
Molten salt
Nuclear reactor
Tribocorrosion
Wear

Access to Document

10.1016/j.wear.2023.204706

Cite this

@article{b185fa3d4e564674b2279fd17a59f5c7,

title = "Tribocorrosion of stainless steel sliding against graphite in FLiNaK molten salt",

abstract = "The molten salt reactor (MSR) concept recently gained renewed interest in developing Generation IV nuclear reactors. One MSR design uses fluoride molten salts to cool tri-structural isotropic particle fuel encapsulated by a carbon matrix into spherical pebbles, which would inevitably contact the reactor's stainless steel container wall during salt circulation. Characterizing this interaction is crucial for reactor safety. Here we report the tribocorrosion behavior of graphite sliding against Type 316H stainless steel lubricated by a FLiNaK (LiF:NaF:KF; 46.5:11.5:42 mol %) molten salt in an argon environment. Accelerated wear loss was observed at a higher temperature because of a lower molten salt viscosity and a higher corrosion rate. The graphite had a more rapid material loss at a higher sliding speed than stainless steel because of its higher vulnerability to vibration-induced microfracture. The salt-starved condition caused more material loss than either the no-salt or the salt-flooded condition because neither a graphite transfer film nor stable boundary lubrication could be established at salt starvation. An interesting dual-layer surface film was discovered on the stainless steel worn surface: a chromium-rich top film and a nickel-accumulated but chromium-depleted interlayer. The film composition and structure provide fundamental insights to the mechanochemical interactions between stainless steel and graphite in a molten salt environment.",

keywords = "Graphite, Molten salt, Nuclear reactor, Tribocorrosion, Wear",

author = "Xin He and Chanaka Kumara and Dino Sulejmanovic and Keiser, {James R.} and Nidia Gallego and Jun Qu",

note = "Publisher Copyright: {\textcopyright} 2023 Elsevier B.V.",

year = "2023",

month = jun,

day = "1",

doi = "10.1016/j.wear.2023.204706",

language = "English",

volume = "522",

journal = "Wear",

issn = "0043-1648",

publisher = "Elsevier",

}

TY - JOUR

T1 - Tribocorrosion of stainless steel sliding against graphite in FLiNaK molten salt

AU - He, Xin

AU - Kumara, Chanaka

AU - Sulejmanovic, Dino

AU - Keiser, James R.

AU - Gallego, Nidia

AU - Qu, Jun

PY - 2023/6/1

Y1 - 2023/6/1

N2 - The molten salt reactor (MSR) concept recently gained renewed interest in developing Generation IV nuclear reactors. One MSR design uses fluoride molten salts to cool tri-structural isotropic particle fuel encapsulated by a carbon matrix into spherical pebbles, which would inevitably contact the reactor's stainless steel container wall during salt circulation. Characterizing this interaction is crucial for reactor safety. Here we report the tribocorrosion behavior of graphite sliding against Type 316H stainless steel lubricated by a FLiNaK (LiF:NaF:KF; 46.5:11.5:42 mol %) molten salt in an argon environment. Accelerated wear loss was observed at a higher temperature because of a lower molten salt viscosity and a higher corrosion rate. The graphite had a more rapid material loss at a higher sliding speed than stainless steel because of its higher vulnerability to vibration-induced microfracture. The salt-starved condition caused more material loss than either the no-salt or the salt-flooded condition because neither a graphite transfer film nor stable boundary lubrication could be established at salt starvation. An interesting dual-layer surface film was discovered on the stainless steel worn surface: a chromium-rich top film and a nickel-accumulated but chromium-depleted interlayer. The film composition and structure provide fundamental insights to the mechanochemical interactions between stainless steel and graphite in a molten salt environment.

AB - The molten salt reactor (MSR) concept recently gained renewed interest in developing Generation IV nuclear reactors. One MSR design uses fluoride molten salts to cool tri-structural isotropic particle fuel encapsulated by a carbon matrix into spherical pebbles, which would inevitably contact the reactor's stainless steel container wall during salt circulation. Characterizing this interaction is crucial for reactor safety. Here we report the tribocorrosion behavior of graphite sliding against Type 316H stainless steel lubricated by a FLiNaK (LiF:NaF:KF; 46.5:11.5:42 mol %) molten salt in an argon environment. Accelerated wear loss was observed at a higher temperature because of a lower molten salt viscosity and a higher corrosion rate. The graphite had a more rapid material loss at a higher sliding speed than stainless steel because of its higher vulnerability to vibration-induced microfracture. The salt-starved condition caused more material loss than either the no-salt or the salt-flooded condition because neither a graphite transfer film nor stable boundary lubrication could be established at salt starvation. An interesting dual-layer surface film was discovered on the stainless steel worn surface: a chromium-rich top film and a nickel-accumulated but chromium-depleted interlayer. The film composition and structure provide fundamental insights to the mechanochemical interactions between stainless steel and graphite in a molten salt environment.

KW - Graphite

KW - Molten salt

KW - Nuclear reactor

KW - Tribocorrosion

KW - Wear

UR - http://www.scopus.com/inward/record.url?scp=85150390360&partnerID=8YFLogxK

U2 - 10.1016/j.wear.2023.204706

DO - 10.1016/j.wear.2023.204706

M3 - Article

AN - SCOPUS:85150390360

SN - 0043-1648

VL - 522

JO - Wear

JF - Wear

M1 - 204706

ER -

Tribocorrosion of stainless steel sliding against graphite in FLiNaK molten salt

Abstract

Funding

Keywords

Access to Document

Other files and links

Fingerprint

Cite this