Abstract
The isothermal section of the Ti-Ni-Si ternary system at 1100 °C was constituted. Twenty-one singlephase areas were determined. The binary Ti3Si phase proposed to occur at 1100 °C was not found in the investigation. A new phase, with the composition of NiTi4Si4 named H, was detected. Some of the ternary compounds show noticeable composition ranges, especially G'-Ni3Ti2Si.