TY - JOUR
T1 - Progress towards a low-cost commercial coated conductor
AU - Annavarapu, Suresh
AU - Nguyen, Nguyet
AU - Cui, Sky
AU - Schoop, Urs
AU - Thieme, Cees
AU - Rupich, Martin W.
AU - Kodenkandath, Thomas
AU - Verebelyi, Darren
AU - Zhang, Wei
AU - Li, Xiaoping
AU - Li, Qi
AU - Paranthaman, Mariappan
AU - Goyal, Amit
AU - Cantoni, Claudia
AU - Kowalewski, Matthew M.
AU - List, Fred A.
PY - 2002
Y1 - 2002
N2 - YBCO films prepared from metal trifluoroacetate (TFA) precursors on oxide-buffered textured non-magnetic substrates have achieved performance levels equaling that on oxide buffered textured Ni substrates. Critical current densities of 0.7 MA/cm2 to 1.0 MA/cm2 have been achieved in 0.4 μm thick YBCO films on short-length of CeO2/YSZ/Y2O3/Ni/Ni-13wt%Cr substrates. High-quality epitaxial buffers comprising a Ni layer, Y2O3 seed, YSZ barrier and CeO2 cap layers have been deposited over meter long tapes of deformation textured Ni and Ni-13%Cr using reel-to-reel processes. High-performance TFA-based YBCO films have been deposited on 0.1 m to 0.3 m lengths of these oxide buffered substrates using reel to reel processes. Critical current densities up to 1.0 MA/cm2 have been achieved in 0.4 μm thick YBCO films on CeO2/YSZ/Y2O3/Ni substrates. Using multiple coats of the metal trifluoroacetate precursors, thicker YBCO films have been demonstrated on oxide buffered substrates. Critical currents in excess of 100A/cm-width have been achieved for 1.2 μm - 1.6 μm thick YBCO films on short lengths of CeO2/YSZ/Y2O3/Ni substrates.
AB - YBCO films prepared from metal trifluoroacetate (TFA) precursors on oxide-buffered textured non-magnetic substrates have achieved performance levels equaling that on oxide buffered textured Ni substrates. Critical current densities of 0.7 MA/cm2 to 1.0 MA/cm2 have been achieved in 0.4 μm thick YBCO films on short-length of CeO2/YSZ/Y2O3/Ni/Ni-13wt%Cr substrates. High-quality epitaxial buffers comprising a Ni layer, Y2O3 seed, YSZ barrier and CeO2 cap layers have been deposited over meter long tapes of deformation textured Ni and Ni-13%Cr using reel-to-reel processes. High-performance TFA-based YBCO films have been deposited on 0.1 m to 0.3 m lengths of these oxide buffered substrates using reel to reel processes. Critical current densities up to 1.0 MA/cm2 have been achieved in 0.4 μm thick YBCO films on CeO2/YSZ/Y2O3/Ni substrates. Using multiple coats of the metal trifluoroacetate precursors, thicker YBCO films have been demonstrated on oxide buffered substrates. Critical currents in excess of 100A/cm-width have been achieved for 1.2 μm - 1.6 μm thick YBCO films on short lengths of CeO2/YSZ/Y2O3/Ni substrates.
UR - http://www.scopus.com/inward/record.url?scp=0036353812&partnerID=8YFLogxK
M3 - Article
AN - SCOPUS:0036353812
SN - 0272-9172
VL - 689
SP - 231
EP - 237
JO - Materials Research Society Symposium - Proceedings
JF - Materials Research Society Symposium - Proceedings
ER -