Heteroepitaxial growth of Ge films on (100) GaAs by pyrolysis of digermane

Pyrolysis of high-purity digermane (Ge₂ H₆) has been used to grow epitaxial Ge films of high crystalline quality on (100) GaAs substrates in a low-pressure environment. X-ray double-crystal diffractometry shows that fully commensurate, coherently strained epitaxial Ge films can be grown on (100) GaAs at digermane partial pressures of 0.05-40 mTorr for substrate temperatures of 380-600°C. Amorphous films also were deposited. Information about the crystalline films surface morphology, growth mode, and microstructure was obtained from scanning electron microscopy, cross-section transmission electron microscopy, and in situ reflectivity measurements. The amorphous-to-crystalline transition temperature and the morphology of the crystalline films were both found to depend on deposition conditions (primarily the incidence rate of Ge-bearing species and the substrate temperature). Epitaxial growth rates using digermane were found to be about two orders of magnitude higher than rates using germane (GeH₄) under similar experimental conditions.