FLiBe Capsule Testing of 316H

This milestone was originally envisioned for completion in FY20 and was delayed due to the COVID-19 response and lack of FLiBe salt. In March 2021, FLiBe salt was received from Kairos Power. The nine capsule experiments with type 316H stainless steel specimens and 316 capsules were completed at 550° and 650°C for 1000 h to bracket the conditions expected in the subsequent thermal convection loop (TCL) experiment. In three capsules, Be metal was added for redox control. The specimen mass losses were low, similar to those observed previously for FLiNaK salt and the addition of Be reduced the average mass loss. Initial characterization suggested that some reaction with Be may have occurred. Therefore, Be was not included in the TCL experiment.