Abstract
Magnons are collective spin excitations in crystals with long-range magnetic order. The emergent van der Waals magnets1–3 provide a highly tunable platform to explore magnetic excitations in the two-dimensional limit with intriguing properties, manifesting from their honeycomb lattice structure and switchable magnetic configurations. Here, we report the direct observation of two-dimensional magnons through magneto-Raman spectroscopy with optical selection rules determined by the interplay between crystal symmetry, layer number and magnetic states in atomically thin CrI3. In monolayers, we observe an acoustic magnon mode at ~0.3 meV. It has strict cross-circularly polarized selection rules locked to the magnetization direction that originates from the conservation of angular momentum of photons and magnons dictated by three-fold rotational symmetry4. Additionally, we reveal optical magnon modes at ~17 meV. This mode is Raman silent in monolayers, but optically active in bilayers and bulk due to a relaxation of the parity criterion resulting from the layer index. In the layered antiferromagnetic states, we directly resolve two degenerate optical magnon modes with opposite angular momentum and conjugate optical selection rules. From these measurements, we quantitatively extract the spin-wave gap, magnetic anisotropy and intralayer and interlayer exchange constants, and establish two-dimensional magnets as a new platform for exploring magnon physics.
Original language | English |
---|---|
Pages (from-to) | 20-25 |
Number of pages | 6 |
Journal | Nature Physics |
Volume | 17 |
Issue number | 1 |
DOIs | |
State | Published - Jan 2021 |
Funding
We thank N. Wilson for helpful discussion. This work was mainly supported by the Department of Energy, Basic Energy Sciences, Materials Sciences and Engineering Division (DE-SC0012509). Device fabrication and understanding of magnon optical selection rules were partially supported by AFOSR MURI 2D MAGIC (FA9550-19-1-0390). Work at ORNL (M.A.M.) was supported by the US Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division. K.W. and T.T. acknowledge support from the Elemental Strategy Initiative conducted by MEXT, Japan, and CREST (JPMJCR15F3), JST. B.H. acknowledges partial support from NW IMPACT. X.X. acknowledges support from the State of Washington funded Clean Energy Institute and from the Boeing Distinguished Professorship in Physics.