Abstract
Here, we present a direct observation of fatigue phenomena in epitaxially grown Pb(Zr0.2Ti0.8)O3 (PZT) thin films using second harmonic piezoresponse force microscopy (SH-PFM). We observed strong correlation between the SH-PFM amplitude and phase signals with the remnant piezoresponse at different switching cycles. The SH-PFM results indicate that the average fraction of switchable domains decreases globally and the phase delays of polarization switching differ locally. In addition, we found that the fatigue developed uniformly over the whole area without developing region-by-region suppression of switchable polarization as in polycrystalline PZT thin films.
| Original language | English |
|---|---|
| Article number | 052904 |
| Journal | Applied Physics Letters |
| Volume | 99 |
| Issue number | 5 |
| DOIs | |
| State | Published - Aug 1 2011 |
Funding
The submitted manuscript has been created by UChicago Argonne, LLC, Operator of Argonne National Laboratory (“Argonne”). Argonne, a U.S. Department of Energy Office of Science laboratory, is operated under Contract No. DE-AC02-06CH11357. The U.S. Government retains for itself, and others acting on its behalf, a paid-up nonexclusive, irrevocable worldwide license in said article to reproduce, prepare derivative works, distribute copies to the public, and perform publicly and display publicly, by or on behalf of the Government. The work at Oak Ridge National Laboratory was sponsored by the U.S. Department of Energy, Basic Energy Sciences, Materials Sciences and Engineering Division. Financial support under the Grant DoE FG02-08ER46526 is acknowledged.