Nanostructured ferritic alloys (NFAs), such as oxide-dispersion strengthened (ODS) alloys, play a vital role in advanced fission and fusion reactors, offering superior properties when incorporating nanoparticles under irradiation. Despite their importance, the high cost of mass-producing NFAs through mechanical milling presents a challenge. This study delves into the microstructure-mechanical property correlations of three NFAs produced using a novel, cost-effective approach combining severe plastic deformation (SPD) with the continuous thermomechanical processing (CTMP) method. Analysis using scanning electron microscopy (SEM)-electron backscatter diffraction (EBSD) revealed nano-grain structures and phases, while scanning transmission electron microscopy (STEM)-energy dispersive X-ray spectroscopy (EDS) quantified the size and density of Ti-N, Y-O, and Cr-O fine particles. Atom probe tomography (APT) further confirmed the absence of finer Y-O particles and characterized the chemical composition of the particles, suggesting possible nitride dispersion strengthening. Correlation of microstructure and mechanical testing results revealed that CTMP alloys, despite having lower nanoparticle densities, exhibit strength and ductility comparable to mechanically milled ODS alloys, likely due to their fine grain structure. However, higher nanoparticle densities may be necessary to prevent cavity swelling under high-temperature irradiation and helium gas production. Further enhancements in uniform nanoparticle distribution and increased sink strength are recommended to mitigate cavity swelling, advancing their suitability for nuclear applications.
Original language | English |
---|---|
Article number | 4763 |
Journal | Materials |
Volume | 17 |
Issue number | 19 |
DOIs | |
State | Published - Oct 2024 |
Funding
This manuscript has been authored by UT-Battelle, LLC, under contract DE-AC05-00OR22725 with the US Department of Energy (DOE). The US government retains and the publisher, by accepting the article for publication, acknowledges that the US government retains a nonexclusive, paid-up, irrevocable, worldwide license to publish or reproduce the published form of this manuscript, or allow others to do so, for US government purposes. DOE will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan ( http://energy.gov/downloads/doe-public-access-plan accessed on 15 July 2024). This research was funded by the US Department of Energy (DOE)\u2019s Fusion Materials Program at Oak Ridge National Laboratory (ORNL), under the contract DE-AC05-00OR22725 with UTBattelle, LLC.
Keywords
- atom probe tomography (APT)
- mechanical properties
- nanostructured ferritic alloys
- nuclear materials
- oxide dispersion strengthened (ODS) alloys
- transmission electron microscopy (TEM)