ASSESSING THE EFFECTIVENESS OF ULTRASONIC IMPACT TREATMENT ON RESIDUAL STRESS PROFILES IN DISSIMILAR WELDED JOINTS

Residual stresses (RS) induced during welding processes are a critical concern in materials engineering, as they can significantly impair the mechanical performance of components by reducing fatigue strength and tensile load capacity. This challenge is especially pronounced in dissimilar metal welds (DMWs), where variations in thermal expansion properties between the joined alloys exacerbate the formation of tensile RS. Conventional post-weld heat treatments, though effective for homogeneous materials, often require substantial energy, specialized equipment, and extensive processing time, making them less practical for DMW applications. Thus, there is a clear need for innovative, energy-efficient techniques to mitigate these detrimental stresses. This study investigates ultrasonic impact treatment (UIT) as a possible alternative for mitigating tensile RS in both similar and dissimilar metal welds. To evaluate UIT's effectiveness, neutron diffraction (ND) was employed as a nondestructive technique to quantify RS in three orthogonal directions-longitudinal, transverse, and normal. The results showed that UIT significantly reduced peak tensile RS, particularly in the longitudinal direction, by up to 180 MPa in similar welds and up to 150 MPa in dissimilar welds. Given the limited literature on UIT application in DMWs, this work contributes valuable data on stress redistribution mechanisms and highlights UIT's potential as a practical stress-relief method. The findings lay the groundwork for further investigations aimed at optimizing process parameters and understanding long-term performance in welded joints.