A new non-PRM bumping process by electroplating on Si Die for three dimensional packaging

Jiheon Jun, Inrak Kim, Michael Mayer, Y. Norman Zhou, Seungboo Jung, Jaepil Jung

Research output: Contribution to journalArticlepeer-review

7 Scopus citations

Abstract

A new bumping process on a Si The by electroplating without a photo-resist-mold (PRM) was assessed for the three dimensional (3D) stacking of Si dice. In this process, solder bumps were deposited selectively onto the surface of a Cu plugged-through silicon-via (TSV) in a Si The. Since lithography related processes to make a PRM for solder bumping were omitted, it can reduce the production time and cost for bumping. The substrate was a Si wafer, and TSVs were produced by deep-ion-reactive-etching (DRIE). As an insulation layer, SiO2 was formed by high-density-plasma-chemical-vapor-deposition (HDPCVD) or wet oxidation method. A Ti adhesion and an Au seed layers were deposited by sputtering. Cu was plugged into the vias by pulsed direct-current (DC) electroplating. The backside of the Si wafer was ground by chemicalmechanical-polishing (CMP). Sn bumps were electroplated on the Cu plugged vias by a current supplied through a Cu-overplated layer (COL) on the vias surface. As experimental results, wet oxidation provided a uniform SiO 2 thickness through the via depth, whereas the SÍO2 thickness by HDPCVD decreased with the via depth. The Ti and Au thicknesses also decreased along the via depth. In electroplating for Cu plugging, defect-free Cu plug was achieved by pulsed DC for 18h, where one cycle composed of a 5 s cathodic term with - 12.2 mA cm-2 and a 25s anodic term with 2.3 mA.cm -2. Sn bumping using COL without PRM was accomplished successfully at a current density of -30mAcm-2 for 15 min. The diameter and height of the Sn bumps ranged from 48.5 to 52 μm and 22 to 25 μm, respectively. The bumps had a rivet head shape without a columnar part and showed facets on the bump surface. The COL was removed by CMP without damage to the bumps.

Original languageEnglish
Pages (from-to)1887-1892
Number of pages6
JournalMaterials Transactions
Volume51
Issue number10
DOIs
StatePublished - Oct 2010
Externally publishedYes

Keywords

  • Copper plugging
  • Electroplating
  • Photo-resist-mold bumping
  • Three dimensional packaging
  • Through silicon via (TSV)