Cellulose molecular weight of corn stover with cotreatment

Here we present a dataset of cellulose molecular weights from corn stover after a cotreatment process. The corn stover sample was subjected to a combination of mechanical disruption (ball milling) and consolidated bioprocessing (CBP) process using the bacterium C. thermocellum at 60 grams/L solids loadings. Cellulose was isolated from control, no cotreatment control, and cotreatment corn stover. Cellulose was then derivatized using anhydrous pyridine and phenyl isocyanate over 48 h at 70 ºC. The reaction was quenched by anhydrous methanol. Methanol and water mixture (7:3, v/v) was added dropwise to promote precipitation of the cellulose derivative. The solids were collected by filtration and thoroughly washed with the methanol and water mixture followed by water. The cellulose derivative was dried overnight under vacuum at 40°C. The obtained cellulose tricarbanilates was then dissolved in tetrahydrofuran (THF) at 1.0 mg/mL and the solution was filtered through a 0.45 µm PTFE filter and placed in an auto-sampler vial. The molecular weight of cellulose was measured by Agilent GPC SECurity 1200 system equipped with four Waters Styragel columns (i.e., HR0.5, HR2, HR4, and HR6) and a UV detector (270 nm). THF was used as the mobile phase. Data collection and processing was performed by Polymer Standards Service WinGPC Unity software (Build 6807). The molecular weight was calculated relative to the polystyrene calibration curve. The data on molecular weights provided information about the effects of cotreatment on corn stover cellulose molecular changes.